Experiments on making a plastic scintillator with polystyrene as a base material mixed with fluor... more Experiments on making a plastic scintillator with polystyrene as a base material mixed with fluorescent compounds (primary and secondary dopants) have been performed. Primary dopants (PTP) used to produce emission at wavelengths of visible light and secondary dopants (POPOP) to shift the visible wavelengths to wavelengths that could be detected by Photomultiplier Tube (PMT) ) were carried out. Experiments were performed on the melting points condition of these materials, which had previously been subjected to a thermo-mechanical analysis using a Thermogravimetric Analysis-Differential Scanning Calorimetry (TGA-DSC) machine, where the melting point was in the range of 200-240°C. Furthermore, the fabrication was carried out using the extrusion technique, where polystyrene pellets mixed with PTP (1.5% by weight) and POPOP (0.05% by weight) were fed into an extrusion machine which has four hot areas to obtain a thin plate plastic scintillator. The plates were then analyzed with a UV-Vis...
Saat Akselerator elektron dioperasikan, akan terjadi interaksi antara berkas elektron yang keluar... more Saat Akselerator elektron dioperasikan, akan terjadi interaksi antara berkas elektron yang keluar dari window terhadap medium udara pada daerah iradiasi dan mengakibatkan terbentuknya gas ozon (O3). Analisis perhitungan yang dilakukan meliputi estimasi ketinggian minimal cerobong pada instalasi AEET 10 MeV untuk memenuhi persyaratan paparan konsentrasi ozon di udara agar tidak melebihi nilai batas yang diizinkan yaitu 0,1 ppm. Untuk melakukan perhitungan tersebut dilakukan dengan menggunakan model dispersi Gauss. Data yang digunakan dalam melakukan pehitungan adalah kecepatan angin minimal adalah 1,5 m/detik dan kecepatan angin maksimal adalah 6 m/detik untuk wilayah sekitar rencana pembangunan akselerator pada saat pagi, siang dan malam hari. Variasi jarak pemaparan menurut arah angin tersebut diambil dari hasil data studi sebelumya yaitu dari 1 meter dengan nilai ozon beserta material campurannya (75% PE, 25% SS), yang salah satu materialnya berasal dari kabel yaitu sebesar 2,35 p...
WAKTU IRADIASI MINIMUM PERGERAKAN TOTE DALAM PROSES IRADIASI IRADIATOR GAMMA MERAH PUTIH. Teknolo... more WAKTU IRADIASI MINIMUM PERGERAKAN TOTE DALAM PROSES IRADIASI IRADIATOR GAMMA MERAH PUTIH. Teknologi pengawetan yang handal saat ini adalah teknologi iradiasi. Teknologi pengawetan sayuran dan buah-buahan dapat menunda waktu pembusukan sehingga sayuran dan buah-buahan dapat di distribusikan dengan lebih baik ke seluruh nusantara maupun diekspor ke luar negeri. Dalam beberapa kasus terutama untuk fitosanitari, dosis iradiasi yang dibutuhkan relative kecil. Salah satu cara untuk menurunkan waktu iradiasi dapat dilakukan dengan merubah desain proses perpindahan tote dengan jumlah langkah minimum, namun tetap semua tote mengalami 72 posisi iradiasi. Proses perpindahan tote sendiri digerakkan oleh sistem pneumatik. Dari hasil analisis dan pembahasan diketahui dengan desain pola pergerakan tote ini diperoleh waktu iradiasi minimum dari 78 menit menjadi 50,4 menit. Waktu siklus minimum dari 65 detik menjadi 42 detik. Jumlah siklus per step dari 9 step menjadi 6 step per siklus. Dosis minimu...
ANALISIS FLEKSIBILITAS PADA SAMBUNGAN SISTEM PEMIPAAN DENGAN BUKAAN SHELL TANGKI DILUTION T100-03... more ANALISIS FLEKSIBILITAS PADA SAMBUNGAN SISTEM PEMIPAAN DENGAN BUKAAN SHELL TANGKI DILUTION T100-03 PROSES PRODUKSI YELLOW CAKE BERDASARKAN API STANDARD 650. Untuk melakukan analisa fleksibilitas terhadap sistem pemipaan diperlukan data/informasi tentang kekakuan di setiap koneksi antar pipa dengan unit operasi, seperti tangki. Khusus untuk tangki, koneksi antar pipa dengan tangki biasanya menggunakan nozzle, karena itu data tentang kekakuan di sekitar nozzle tangki harus ada untuk masukan pada analisis fleksibilitas pipa. Dari hasil perhitungan didapat nilai koefisien kekakuan sebesar KR = 3,65 x 104 N.mm, KL = 3,3 x 105 N.mm/rad dan KC = 6,7 x 105 N.mm/rad. Pertumbuhan shell ke arah radial adalah W = 0,66 mm dan Rotasi Shell -0,001 rad. Hasil perhitungan Caesar II menunjukkan untuk Fx, Fy, Fz masing-masing sebesar 30 N,-493 N, -11 N. Sedangkan untuk moment Mx, My, Mz masing-masing sebesar -97 Nmm, 39 Nmm, 457 Nmm. Gaya dan moment hasil keluaran caesar di masukkan dalam persamaan unt...
Experiments on making a plastic scintillator with polystyrene as a base material mixed with fluor... more Experiments on making a plastic scintillator with polystyrene as a base material mixed with fluorescent compounds (primary and secondary dopants) have been performed. Primary dopants (PTP) used to produce emission at wavelengths of visible light and secondary dopants (POPOP) to shift the visible wavelengths to wavelengths that could be detected by Photomultiplier Tube (PMT) ) were carried out. Experiments were performed on the melting points condition of these materials, which had previously been subjected to a thermo-mechanical analysis using a Thermogravimetric Analysis-Differential Scanning Calorimetry (TGA-DSC) machine, where the melting point was in the range of 200-240°C. Furthermore, the fabrication was carried out using the extrusion technique, where polystyrene pellets mixed with PTP (1.5% by weight) and POPOP (0.05% by weight) were fed into an extrusion machine which has four hot areas to obtain a thin plate plastic scintillator. The plates were then analyzed with a UV-Vis...
Saat Akselerator elektron dioperasikan, akan terjadi interaksi antara berkas elektron yang keluar... more Saat Akselerator elektron dioperasikan, akan terjadi interaksi antara berkas elektron yang keluar dari window terhadap medium udara pada daerah iradiasi dan mengakibatkan terbentuknya gas ozon (O3). Analisis perhitungan yang dilakukan meliputi estimasi ketinggian minimal cerobong pada instalasi AEET 10 MeV untuk memenuhi persyaratan paparan konsentrasi ozon di udara agar tidak melebihi nilai batas yang diizinkan yaitu 0,1 ppm. Untuk melakukan perhitungan tersebut dilakukan dengan menggunakan model dispersi Gauss. Data yang digunakan dalam melakukan pehitungan adalah kecepatan angin minimal adalah 1,5 m/detik dan kecepatan angin maksimal adalah 6 m/detik untuk wilayah sekitar rencana pembangunan akselerator pada saat pagi, siang dan malam hari. Variasi jarak pemaparan menurut arah angin tersebut diambil dari hasil data studi sebelumya yaitu dari 1 meter dengan nilai ozon beserta material campurannya (75% PE, 25% SS), yang salah satu materialnya berasal dari kabel yaitu sebesar 2,35 p...
WAKTU IRADIASI MINIMUM PERGERAKAN TOTE DALAM PROSES IRADIASI IRADIATOR GAMMA MERAH PUTIH. Teknolo... more WAKTU IRADIASI MINIMUM PERGERAKAN TOTE DALAM PROSES IRADIASI IRADIATOR GAMMA MERAH PUTIH. Teknologi pengawetan yang handal saat ini adalah teknologi iradiasi. Teknologi pengawetan sayuran dan buah-buahan dapat menunda waktu pembusukan sehingga sayuran dan buah-buahan dapat di distribusikan dengan lebih baik ke seluruh nusantara maupun diekspor ke luar negeri. Dalam beberapa kasus terutama untuk fitosanitari, dosis iradiasi yang dibutuhkan relative kecil. Salah satu cara untuk menurunkan waktu iradiasi dapat dilakukan dengan merubah desain proses perpindahan tote dengan jumlah langkah minimum, namun tetap semua tote mengalami 72 posisi iradiasi. Proses perpindahan tote sendiri digerakkan oleh sistem pneumatik. Dari hasil analisis dan pembahasan diketahui dengan desain pola pergerakan tote ini diperoleh waktu iradiasi minimum dari 78 menit menjadi 50,4 menit. Waktu siklus minimum dari 65 detik menjadi 42 detik. Jumlah siklus per step dari 9 step menjadi 6 step per siklus. Dosis minimu...
ANALISIS FLEKSIBILITAS PADA SAMBUNGAN SISTEM PEMIPAAN DENGAN BUKAAN SHELL TANGKI DILUTION T100-03... more ANALISIS FLEKSIBILITAS PADA SAMBUNGAN SISTEM PEMIPAAN DENGAN BUKAAN SHELL TANGKI DILUTION T100-03 PROSES PRODUKSI YELLOW CAKE BERDASARKAN API STANDARD 650. Untuk melakukan analisa fleksibilitas terhadap sistem pemipaan diperlukan data/informasi tentang kekakuan di setiap koneksi antar pipa dengan unit operasi, seperti tangki. Khusus untuk tangki, koneksi antar pipa dengan tangki biasanya menggunakan nozzle, karena itu data tentang kekakuan di sekitar nozzle tangki harus ada untuk masukan pada analisis fleksibilitas pipa. Dari hasil perhitungan didapat nilai koefisien kekakuan sebesar KR = 3,65 x 104 N.mm, KL = 3,3 x 105 N.mm/rad dan KC = 6,7 x 105 N.mm/rad. Pertumbuhan shell ke arah radial adalah W = 0,66 mm dan Rotasi Shell -0,001 rad. Hasil perhitungan Caesar II menunjukkan untuk Fx, Fy, Fz masing-masing sebesar 30 N,-493 N, -11 N. Sedangkan untuk moment Mx, My, Mz masing-masing sebesar -97 Nmm, 39 Nmm, 457 Nmm. Gaya dan moment hasil keluaran caesar di masukkan dalam persamaan unt...
Uploads
Papers by Hana Subhiyah